JIS C 2105:2019 電気絶縁用無溶剤液状レジン試験方法 | ページ 2

                                                                                              3
                                                                                   C 2105 : 2019
      注記 対応国際規格 : ISO 584:1982,Plastics−Unsaturated polyester resins−Determination of reactivity
             at 80 degrees C (conventional method),ISO 1675:1985,Plastics−Liquid resins−Determination of
             density by the pyknometer method,ISO 2114:2000,Plastics (Polyester resins)   nd paints and
             varnishes (binders)−Determination of partial acid value and total acid value,ISO 2535:2001,
             Plastics−Unsaturated-polyester resins−Measurement of gel time at ambient temperature,ISO
             2554:1997,Plastics−Unsaturated polyester resins−Determination of hydroxyl value,ISO
             3521:1997,Plastics−Unsaturated polyester and epoxy resins−Determination of overall volume
             shrinkage及びISO 4615:1979,Plastics−Unsaturated polyesters and epoxide resins−Determination
             of total chlorine content
    JIS K 7100 プラスチック−状態調節及び試験のための標準雰囲気
      注記 対応国際規格 : ISO 291,Plastics−Standard atmospheres for conditioning and testing
    JIS K 7111-1 プラスチック−シャルピー衝撃特性の求め方−第1部 : 非計装化衝撃試験
      注記 対応国際規格 : ISO 179-1:2010,Plastics−Determination of Charpy impact properties−Part 1:
             Non-instrumented impact test(MOD)
    JIS K 7111-2 プラスチック−シャルピー衝撃特性の求め方−第2部 : 計装化衝撃試験
      注記 対応国際規格 : ISO 179-2:1997,Plastics−Determination of Charpy impact properties−Part 2:
             Instrumented impact test(IDT)
    JIS K 7112 プラスチック−非発泡プラスチックの密度及び比重の測定方法
    JIS K 7114 プラスチック−液体薬品への浸せき効果を求める試験方法
      注記 対応国際規格 : ISO 175: 2010,Plastics−Methods of test for the determination of the effects of
             immersion in liquid chemicals
    JIS K 7117-1 プラスチック−液状,乳濁状又は分散状の樹脂−ブルックフィールド形回転粘度計によ
        る見掛け粘度の測定方法
      注記 対応国際規格 : ISO 2555:1989,Plastics−Resins in the liquid state or as emulsions or dispersions
             −Determination of apparent viscosity by the Brookfield test method
    JIS K 7117-2 プラスチック−液状,乳濁状又は分散状の樹脂−回転粘度計による定せん断速度での粘
        度の測定方法
      注記 対応国際規格 : ISO 3219:1993,Plastics−Polymers/resins in the liquid state or as emulsions or
             dispersions−Determination of viscosity using a rotational viscometer with defined shear rate
    JIS K 7161-1 プラスチック−引張特性の求め方−第1部 : 通則
      注記 対応国際規格 : ISO 527-1:1993,Plastics−Determination of tensile properties−Part 1: General
             principles
    JIS K 7161-2 プラスチック−引張特性の求め方−第2部 : 型成形,押出成形及び注型プラスチック
        の試験条件
      注記 対応国際規格 : ISO 527-2:1993,Plastics−Determination of tensile properties−Part 2: Test
             conditions for moulding and extrusion plastics
    JIS K 7171 プラスチック−曲げ特性の求め方
      注記 対応国際規格 : ISO 178:2010,Plastics−Determination of flexural properties
    JIS K 7181 プラスチック−圧縮特性の求め方
      注記 対応国際規格 : ISO 604:2002,Plastics−Determination of compressive properties

――――― [JIS C 2105 pdf 6] ―――――

4
C 2105 : 2019
    JIS K 7191-1 プラスチック−荷重たわみ温度の求め方−第1部 : 通則
      注記1 対応国際規格 : ISO 75-1:2013,Plastics−Determination of temperature of deflection under load
              −Part 1: General test method
      注記2 この規格の対応国際規格ISO 75は,ISO 75-1,ISO 75-2及びISO 75-3に置き換えられて
              おり,ここではISO 75-1に対応したJISとしてJIS K 7191-1を記載している。
    JIS K 7191-2 プラスチック−荷重たわみ温度の求め方−第2部 : プラスチック及びエボナイト
      注記1 対応国際規格 : ISO 75-2:2013,Plastics−Determination of temperature of deflection under load
              −Part 2: Plastics and ebonite
      注記2 この規格の対応国際規格ISO 75は,ISO 75-1,ISO 75-2及びISO 75-3に置き換えられて
              おり,ここではISO 75-2に対応したJISとしてJIS K 7191-2を記載している。
    JIS K 7191-3 プラスチック−荷重たわみ温度の求め方−第3部 : 高強度熱硬化性樹脂積層材及び長
        繊維強化プラスチック
      注記1 対応国際規格 : ISO 75-3:2004,Plastics−Determination of temperature of deflection under load
              −Part 3: High-strength thermosetting laminates and long-fibre-reinforced plastics
      注記2 この規格の対応国際規格ISO 75は,ISO 75-1,ISO 75-2及びISO 75-3に置き換えられて
              おり,ここではISO 75-3に対応したJISとしてJIS K 7191-3を記載している。
    JIS K 7206 プラスチック−熱可塑性プラスチック−ビカット軟化温度(VST)の求め方
      注記 対応国際規格 : ISO 306:2004,Plastics−Thermoplastic materials−Determination of Vicat softening
             temperature (VST)
    JIS K 7209 プラスチック−吸水率の求め方
      注記 対応国際規格 : ISO 62:2008,Plastics−Determination of water absorption(IDT)
    JIS K 7215 プラスチックのデュロメータ硬さ試験方法
      注記 対応国際規格 : ISO 868:2003,Plastics and ebonite−Determination of indentation hardness by
             means of a durometer (Shore hardness)
    JIS K 7236 エポキシ樹脂のエポキシ当量の求め方
      注記 対応国際規格 : ISO 3001:1997,Plastics−Epoxide compounds−Determination of epoxide
             equivalent
    JIS K 7243-1:2005 エポキシ樹脂の塩素含有量の求め方−第1部 : 無機塩素
      注記1 対応国際規格 : ISO 21627-1:2002,Plastics−Epoxy resins−Determination of chlorine content
              −Part 1: Inorganic chlorine
      注記2 この規格の対応国際規格ISO 21627-1は,ISO 4573から置き換えられており,ここではISO
              21627-1に対応したJISとしてJIS K 7243-1を記載している。
    JIS K 7243-2:2005 エポキシ樹脂の塩素含有量の求め方−第2部 : 易可けん化塩素
      注記1 対応国際規格 : ISO 21627-2:2002,Plastics−Epoxy resins−Determination of chlorine content
              −Part 2: Easily saponifiable chlorine
      注記2 この規格の対応国際規格ISO 21627-2は,ISO 4583から置き換えられており,ここではISO
              21627-2に対応したJISとしてJIS K 7243-2を記載している。
    JIS K 7245 プラスチック−エポキシ樹脂用アミン系硬化剤−第一,第二,第三アミノ基窒素含有量
        の求め方
      注記 対応国際規格ISO 9702:1996,Plastics−Amine epoxide hardeners−Determination of primary,

――――― [JIS C 2105 pdf 7] ―――――

                                                                                              5
                                                                                   C 2105 : 2019
             secondary and tertiary amine group nitrogen content
    JIS K 7250-1:2006 プラスチック−灰分の求め方−第1部 : 通則
      注記 対応国際規格 : ISO 3451-1:1997,Plastics−Determination of ash−Part 1: General methods
    JIS Z 2911 かび抵抗性試験方法
      注記 対応国際規格 : IEC 60068-2-10:2005,Environmental testing−Part 2-10: Tests−Test J and
             guidance: Mould growth
    IEC 60050 (all parts),International Electrotechnical Vocabulary
    IEC 60296:2012,Fluids for electrotechnical applications−Unused mineral insulating oils for transformers and
        switchgear
    IEC 60426,Electrical insulating materials−Determination of electrolytic corrosion caused by insulating
        materials−Test methods
    IEC 60455-1:1998,Resin based reactive compounds used for electrical insulation−Part 1: Definitions and
        general requirements
    IEC 60455-3 (all parts),Resin based reactive compounds used for electrical insulation−Part 3: Specifications
        for individual materials
    IEC 60814,Insulating liquids−Oil-impregnated paper and pressboard−Determination of water by automatic
        coulometric Karl Fischer titration
    IEC 61099,Insulating liquids−Specifications for unused synthetic organic esters for electrical purposes
    ISO 1183-1,Plastics−Methods for determining the density of non-cellular plastics−Part 1: Immersion method,
        liquid pyknometer method and titration method
    ISO 1523:2002,Determination of flashpoint−Closed cup equilibrium method
    ISO 2039-1:1993,Plastics−Determination of hardness−Part 1: Ball indentation method
    ISO 4895,Plastics−Liquid epoxy resins−Determination of tendency to crystallize
    ISO 6271,Clear liquids−Estimation of colour by the platinum-cobalt colour scale
    ISO 7327,Plastics−Hardeners and accelerators for epoxide resins−Determination of free acid in acid
        anhydride
    ISO 8987,Plastics−Phenolic resins−Determination of reactivity on a B-transformation test plate
    ISO 9396,Plastics−Phenolic resins−Determination of the gel time of resols under specific conditions using
        automatic apparatus
    ISO 11357-2,Plastics−Differential scanning calorimetry (DSC)−Part 2: Determination of glass transition
        temperature
    ISO 11359-2:1999,Plastics−Thermomechanical analysis (TMA)−Part 2: Determination of coefficient of
        linear thermal expansion and glass transition temperature
    ISO 11359-3,Plastics−Thermomechanical analysis (TMA)−Part 3: Determination of penetration temperature
    ISO 14896,Plastics−Polyurethane raw materials−Determination of isocyanate content

3 用語及び定義

  この規格で用いる主な用語及び定義は,IEC 60455-l:1998及びIEC 60050 (all parts)によるほか,次によ
る。

――――― [JIS C 2105 pdf 8] ―――――

6
C 2105 : 2019
3.1
体積抵抗(volume resistance)
  表面電流を除き,その絶縁体の内部を通って流れる電流分に相当する絶縁抵抗。
3.2
体積抵抗率(volume resistivity)
  単位体積当たりに換算した体積抵抗。
3.3
誘電正接,tan δ(dielectric dissipation factor)
  複素誘電率の中の実数部分に対する虚数部分の比の数値。
3.4
比誘電率,εr(relative permittivity)
  絶対誘電率と電気定数(真空の誘電率)との比。
    注記 実務の場では,比誘電率を指して“誘電率”という用語を用いるのが一般的である。
3.4A
逸散量(emissions)
  電気絶縁用無溶剤レジンの硬化時に,意図しない揮発などで逸散する質量。

4 試験方法に関する一般注意事項

4.1 準備及び条件

  この規格及び関係する規格で規定がない場合,全ての試験は温度25 ℃±4 ℃,相対湿度45 %70 %の
雰囲気条件で行う。測定を行う前に,試料及び試験片は,この雰囲気で試料又は試験片が安定するまでの
時問,予備調整を行う。液状又はペースト状の試料の採取は,JIS K 5600-1-2による。試料の調製は,JIS
K 5600-1-3による。
    注記 標準雰囲気についての用語の定義は,ISO 558を参照。上記に規定する試験雰囲気は,JIS K 7100
          に規定する2種類の標準雰囲気に従っていないが,その許容差を含めた範囲を満足している。
  通常の試験方法に関する要求事項は,この規格で全て規定している。また,図は,単に試験が可能な装
置の一例を示しているだけである。この規格とIEC 60455-3の各シート及び個別材料規格とが不整合な場
合は,後者を優先する。
  試験方法として別の規格を引用する場合には,その規格を引用したことを試験結果に記録する。

4.2 試験順序

  試験を効率的に行うため,試験は次の順序で実施する。
a) 硬化剤混合前の個別成分の試験
b) 硬化剤を混合した後の試験
c) 硬化物についての試験
d) 前処理(熱,湿気,水など)後の硬化物の試験

4.3 試験報告書

  測定値,試験条件などを記録した試験結果を基に,受渡当事者間の取決めに従い,試験報告書を作成す
る。特に指定がない限り,試験報告書には次のデータを記載する。
a) 樹脂の指定及び識別
b) ロット番号又はその他の識別

――――― [JIS C 2105 pdf 9] ―――――

                                                                                              7
                                                                                   C 2105 : 2019
c) 安全データシート(SDS)に従った識別及び表示の確認
d) 試験結果
e) 調整及び校正を含む主要な試験条件
f)  反応性樹脂組成物の処理条件
g) 技術資料(TDS)及びSDSのコピー

5 反応性樹脂組成物及びその成分の試験方法

5.1 引火点

  温度79 ℃未満の引火点の試験方法は,ISO 1523:2002によるとともにその規格の附属書Aに記載するク
ローズドカップ装置のいずれかを用いる。ISO 1523:2002は,JIS K 2265-2[迅速平衡法1)]と併せて用い
る。
  温度79 ℃以上の引火点の試験方法は,JIS K 2265-4(クリーブランド開放式引火点試験方法)による。
  別々の2個の試料で2回測定し,それぞれの測定結果を適用した規格とともに試験結果に記録する。
    注記 引火点が未知のものについて試験する場合は,あらかじめ予備試験を行って,適切な試験方法
          を選択することが望ましい。
    注1) 迅速平衡法はセタ密閉式ともいう。

5.2 密度

  密度の測定は,JIS K 6901の5.1による。測定は2回行い,それぞれの測定結果を適用した規格ととも
に試験結果に記録する。

5.2A 比重

  比重の測定は,JIS C 2103の5.2.2による。測定は2回行い,測定結果を適用した規格とともに試験結果
に記録する。

5.3 粘度

  粘度の測定は,適切な装置を用いて温度23 ℃±0.5 ℃又は受渡当事者間で取り決めた温度で行う。回転
式装置を用いる場合,JIS K 7117-1又はJIS K 7117-2による。エフラックス式の装置を用いる場合,試験
方法及び用いるフローカップはJIS K 5600-2-2による。
  測定は,2回行いそれぞれの測定結果を適用した規格及び試験温度とともに試験結果に記録する。

5.4 高温保存後の粘度

  この試験は,一液系又は硬化剤を混合した組成物には適用しない。
  特に指定しない場合は,十分な量のサンプルを密封容器に入れ,100 ℃±3 ℃の温度で20時間±0.5時
間保存する。室温まで冷却した後,5.3で規定する方法によって粘度を測定する。測定は2回行い,それぞ
れの測定結果を適用した規格とともに試験結果に記録する。粘度の上昇率は,次式を用いて計算する。
                        粘度の上昇率(%)=(η2−η1)×100/η1
                      ここに,   η1 :  高温保存前の初期粘度
                                 η2 :  高温保存後の粘度
    注記 揮発性の高い材料を含有する場合は,内圧上昇による破裂の危険がある。

5.5 揮発性有機成分の含有率

  この試験は,一液系又は硬化剤を混合した組成物には適用しない。特に指定しない場合は,次の試験方
法を用いる。
  空のひょう(秤)量瓶(約80 mm×30 mm)の質量を0.001 g単位まで計量する(m1)。ひょう(秤)量